The Environment-Induced Cracking of as-Annealed Ni3(Si, Ti) and Ni3(Si, Ti) with...

The environment-induced cracking (EIC) of as-annealed Ni3(Si,Ti) and Ni3(Si,Ti) ...

The influences of applied stress, test temperature, and concentration on environ...

The environment-induced cracking (EIC) behavior of Ni3 (Si,Ti) intermetallic com...

The Influences of Applied Stress, Test Temperature, and Concentration on Environ...

The environment-induced cracking (EIC) behavior of Ni3(Si,Ti) intermetallic comp...

Corrosion Behavior of Ni3(Si,Ti) + 2Mo in Hydrochloric Acid Solution

The corrosion behavior of Ni3(Si,Ti) + 2Mo intermetallic compound (L12 and (L12 ...

Corrosion Behavior of Ni3(Si,Ti) in Hydrochloric Acid Solution

The corrosion behaviour of the intermetallic compounds Ni3(Si,Ti) (L12: single p...

INFORMASI: Data berikut ini masih dalam proses pemenuhan Prinsip SDI.

The Environment-Induced Cracking of As-Cold Rolled Ni3(Si,Ti) and Ni3(Si,Ti) with 2Mo in Sodium Chloride Solutions

Terbatas

The environment-induced cracking (EIC) of as cold-rolled Ni3(Si,Ti) and Ni3(Si,Ti) with 2Mo has been investigated as functions of applied stress, chloride ion concentration, test temperature, and pH by using a constant load method in NaCl solutions. The EIC susceptibility of both intermetallic compounds increased with increasing Cl ion concentration and test temperature; and increased with decreasing pH. Both intermetallic compounds had the same transgranular fracture appearance and the relationship between log tf (time to failure) and log lss (steady state elongation rate) became the identical straight line irrespective of applied stress, Cl ion concentration, test temperature, and pH, which means that lss becomes a relevant parameter for predicting tf. The EIC susceptibility of Ni3(Si,Ti) with 2Mo was lower than that of Ni3(Si,Ti), which showed the beneficial effect of Mo. From the results obtained, EIC of both intermetallic compounds was presumed to take place by hydrogen embrittlement (HE). Journal of Alloys and Compounds, Vol. 639. Hal. 504–510

Data and Resources

Metadata

Version
Produsen Data
Email Produsen Data
Walidata
Email Walidata
Periode Data
Akses Data
Kode Daftar Data
Kode Indikator MMS
Kode Standar Data
Satuan
Ukuran
Jenis Data
Kategori
Data Prioritas
Kriteria Prioritas
Indikator Prioritas
Kode Metadata Kegiatan